Corrosion of a spark plasma sintered Fe-Cr-Mo-B-C alloy in 3.5% NaCl solution

Authors

• Mudassir Farooq
• Sohail Muhammad
• A. A. Sorour

Publication Date

2023

Abstract

In this study, the corrosion behavior of a Fe-Cr-Mo-B-C alloy, fabricated by spark plasma sintering of an amorphous alloy powder, in 3.5% NaCl solution was analyzed. Electrochemical impedance spectroscopy and potentiodynamic polarization are techniques which were used for electrochemical performance estimation of samples and the results were further compared with conventional alloys: 1080 carbon steel and 304 stainless steel. Corrosion surface products were characterized through Scanning electron microscopy, Energy dispersive x-ray spectroscopy and X-ray photoelectron spectroscopy. Specimens sintered at 800℃ (S1-800) had achieved 94% densification approximately while the sample sintered at 900℃ (S2-900), had densified more which was 98% approximately. S2-900 had better corrosion resistance than S1-800 while in comparison to conventional alloys; it was inferior to 304 stainless steel. It was concluded that the increase in density of sintered samples favoured the formation of more uniform surface products and enhanced the formation of the passive chromium oxide (Cr2O3) layer.

DOI

10.55713/jmmm.v33i1.1588

First Page

27

Last Page

38

Recommended Citation

Farooq, Mudassir; Muhammad, Sohail; and Sorour, A. A. (2023) "Corrosion of a spark plasma sintered Fe-Cr-Mo-B-C alloy in 3.5% NaCl solution," Journal of Metals, Materials and Minerals: Vol. 33: No. 1, Article 5.
DOI: 10.55713/jmmm.v33i1.1588
Available at: https://digital.car.chula.ac.th/jmmm/vol33/iss1/5