Journal of Metals, Materials and Minerals

Publication Date

2022

Abstract

Oil palm frond waste was used as reinforcing fibers for biodegradable poly(lactic acid) or PLA in order to produce green composites that increased the value of agricultural waste. The alkali-treated oil palm frond (OPF) fibers of 30 wt% or 40 wt% were compounded with PLA and moulded into specimens. The alkali treatment was 0 wt%, 1 wt%, 3 wt%, and 5 wt% of the fibers for compatibility improvement with PLA matrix. It was found that the alkali-treated PLA/OPF composites adding 30 wt% and 40 wt% had the flexural modulus to be about 55% and 75% higher than those without the treatment, respectively. Tensile modulus of the composites was also increased. Nevertheless, the higher rigidity composites became more brittle as evident by the fracture toughness testing. The increase of total breaking energy confirmed the better interfacial adhesion between phases as shown in SEM micrographs. The glass transition temperature (Tg) of PLA matrix in the composites was shifted to lower temperature attributed to the thermal degradation of PLA during the melt compounding confirmed by the lower degradation temperature. Increasing the alkali concentration for surface treatment caused the Tg of PLA composites to be higher, supporting that the improvement of interfacial adhesion was achieved.

DOI

10.55713/jmmm.v32i1.1244

First Page

134

Last Page

143

Download

Share

COinS
 
 

To view the content in your browser, please download Adobe Reader or, alternately,
you may Download the file to your hard drive.

NOTE: The latest versions of Adobe Reader do not support viewing PDF files within Firefox on Mac OS and if you are using a modern (Intel) Mac, there is no official plugin for viewing PDF files within the browser window.