Effect of cladding of stellite-6 filler wire on the surface of ss316l alloy through cold metal arc transfer process

Authors

• Thinesh Babu Thiagarajan
• Sengottuvel Ponnusamy

Publication Date

2021

Abstract

In this work, Cladding was done on SS316L alloy through the CMT process using Stellite-6 filler wire. 31 experiments were done at different welding conditions as per CCD matrix. The cladding specimens were characterized by macro and micro-study, Vickers microhardness evaluation and corrosion resistance analysis. An optical microscope, SEM-EDAX, and XRD were used to predict the structural characterizations, presence and the distributions of the elements. Based on the study higher voltage & welding speed showed appreciable hardness at the interface & cladding regions. The thickness of the interface was noted at a maximum of 190 μm. The EDS spectra showed that Fe, Cr and Co were the major elements in the clad and interface regions. The Co-rich phase and the low content of element O are found in the low corroded regions on the specimen. The maximum hardness observed at cladding and interface were 378 Hv and 270 Hv respectively.

DOI

10.55713/jmmm.v31i3.1197

First Page

70

Last Page

84

Recommended Citation

Thiagarajan, Thinesh Babu and Ponnusamy, Sengottuvel (2021) "Effect of cladding of stellite-6 filler wire on the surface of ss316l alloy through cold metal arc transfer process," Journal of Metals, Materials and Minerals: Vol. 31: No. 3, Article 9.
DOI: 10.55713/jmmm.v31i3.1197
Available at: https://digital.car.chula.ac.th/jmmm/vol31/iss3/9