Abstract

Aluminum dross is a hazardous byproduct from aluminum industry that causes environmental problems and high disposal cost. This work presents a sustainable route to upcycle secondary aluminum dross into lightweight ceramic foams for insulating refractory applications. Secondary aluminum dross powder was blended with polyethylene (PE) pore-forming agents (30 vol% to 70 vol%) and polyvinyl alcohol (PVA) binder added as a 7.5 wt% aqueous solution (binder contents: 1 vol% and 3 vol%), followed by pressing and sintering at 1400℃. Increasing PE systematically reduced bulk density and increased open porosity. At 70 vol% PE, the foams reached a bulk density of 0.94 g∙cm‒3 and open porosity of ~74%, satisfying the Japanese Industrial Standard (JIS) specification for lightweight refractory bricks. The maximum compressive strength was ~2 MPa, sufficient for thermal insulation where load-bearing capacity is secondary. X-ray diffraction confirmed a multiphase matrix of α−Al2O3, MgAl2O4, and CaAl12O19, indicating solid-state reactions between alumina and Mg/Ca-bearing phases. Morphology revealed a well-connected porous network stabilized by reaction-bonded bridges, indicating strong interparticle bonding and limited pore coalescence during sintering. This approach can divert over 1000 kg of hazardous waste per ton of secondary aluminum dross processed and cut CO2 emissions by 65% versus alumina routes. The approach promotes circular economy through waste-derived ceramics.

DOI

10.55713/jmmm.v36i3.2549

First Page

1

Last Page

10

Download

Share

COinS
 
 

To view the content in your browser, please download Adobe Reader or, alternately,
you may Download the file to your hard drive.

NOTE: The latest versions of Adobe Reader do not support viewing PDF files within Firefox on Mac OS and if you are using a modern (Intel) Mac, there is no official plugin for viewing PDF files within the browser window.