Abstract

The photocatalytic activity (PA) by electrochromic (EC) enhancement of single and multilayer films of TiO2, WO3, TiO2/WO3, and WO3/TiO2 was investigated. All films were deposited from metal on an ITO glass substrate using direct current (DC) magnetron sputtering via an oblique angle deposition (OAD) technique at 85°. Subsequently, a thermal oxidation (TO) process at 500℃ was applied for the samples to form metal oxide films. The morphology, elemental composition, crystal structure, and optical properties were studied by using field emission scanning electron microscopy (FE-SEM), energy-dispersive X-ray spectroscopy (EDS), X-ray diffractometry (XRD), and UV-vis spectroscopy, respectively. The photocatalytic properties were investigated by showing the degradation rate of methylene blue (MB) solution as an organic pollutant that was examined under ultraviolet irradiation of 300 µW∙cm‒2. The film samples were investigated by comparing the pre-color and colored states that were achieved through the EC process. The EC properties of WO3 led to increased charge insertion on the film surface. This observation was further supported by cyclic voltammetry (CV) testing, which revealed a higher current density for the thin film samples. The photodegradation results showed that the samples in the colored state exhibited a significantly higher degradation rate of MB compared to the pre-color state.

DOI

10.55713/jmmm.v34i4.1964

First Page

-

Last Page

-

Download

Share

COinS
 
 

To view the content in your browser, please download Adobe Reader or, alternately,
you may Download the file to your hard drive.

NOTE: The latest versions of Adobe Reader do not support viewing PDF files within Firefox on Mac OS and if you are using a modern (Intel) Mac, there is no official plugin for viewing PDF files within the browser window.